Title: Avaliação in vitro da microdureza do esmalte e da microinfiltração adjacente a restaurações com cimento de ionômero de vidro após desafio cariogênico: estudo no MEV
Other Titles: In vitro evaluation of enamel microhardness and microleakage adjacent to restorations with glass ionomer cement after cariogenic challenge: MEV study
Authors: Braz, Carolina Pio da Silva
metadata.dc.contributor.advisor: Coutinho, Thereza Christina Lopes
Issue Date: 2018
Abstract: Os objetivos deste estudo foram verificar a microdureza longitudinal (ML) e a microinfiltração marginal (MM) no esmalte adjacente a restaurações, após desafio cariogênico in vitro. Foram utilizados blocos de esmalte bovino, restaurados com cimentos de ionômero de vidro (CIV) e resina composta sem flúor e submetidos a ciclagens de pH. O grupo de controle negativo foi mantido apenas em saliva artificial. Após, todos os blocos foram imersos em corante, seccionados e o grau de MM medido através de escores. Para determinar a ML, foi utilizado um microdurômetro Knoop nas profundidades de 25µm, 75µm e 150µm. Cinco amostras de cada grupo foram avaliadas qualitativamente no MEV (20x e 80x). Os dados foram analisados estatisticamente no software SPSS for Windows v. 20 através dos testes nãoparamétricos de Kruskal-Wallis e de Mann-Whitney. Em relação à MM, observou-se que nenhum dos materiais impediu totalmente a penetração do corante, sendo que, dentre os CIVs testados, o que obteve melhor desempenho foi o Maxxion R (G4), seguido pelo ION-Z (G1) e Vitro Fil® R (G2), no entanto, sem diferença significativa entre eles. Quanto à ML, o G4, G1 e o Vitro Fil® LC (G5) obtiveram os resultados mais altos de dureza dentre os materiais testados. Em relação à análise do MEV, observouse a presença de fendas nas margens das restaurações, independente do material. Conclui-se que, o Maxxion R e o ION-Z demonstraram bom potencial para prevenção da microinfiltração e da ocorrência de cárie no esmalte adjacente à restauração, mesmo em condições de alto desafio cariogênico.
metadata.dc.description.abstractother: The purpose of this work was to verify the longitudinal microhardness (LM) and the marginal microleakage (MM) in the enamel adjacent to restoration after cariogenic challenge in vitro. Blocks of bovine enamel were used, restored with glass ionomer (GI) and composite resin without fluoride and submitted of pH cycling. The negative control group was maintained only in artificial saliva. After, all blocks were immersed in dye, sectioned and the degree of MM was measured through scores. To determine LM, a Knoop microhardness tester was used in depths of 25μm, 75μm and 150μm. Five samples from each group were qualitatively evaluated by SEM (20x and 80x). The data were analyzed statistically in SPSS for Windows v. 20 software through nonparametric Kruskal-Wallis and Mann-Whitney tests. Regarding MM, it was observed that none of the materials completely prevented the penetration of the dye, and among the GIs tested, the one that obtained the best performance was Maxxion R (G4), followed by ION-Z (G1) and Vitro Fil® R (G2), however, with no significant difference among them. As for LM, G4, G1 and Vitro Fil® LC (G5) obtained the highest hardness results among the tested materials. Regarding the SEM analysis, the presence of gaps was observed in the margins of the restorations independent of the material. It was concluded that Maxxion R and ION-Z demonstrated good potential for the prevention of microleakage and the occurrence of caries in the enamel adjacent to the restoration, even in conditions of high cariogenic challenge.
URI: https://app.uff.br/riuff/handle/1/10096
Appears in Collections:PPGO - Teses e Dissertações

Files in This Item:
File Description SizeFormat 
DISSERTAÇÃO CAROLINA BRAZ.pdf1.01 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons