Title: Estudo das propriedades mecânica e de grupos funcionais de um novo nanocompósito para aplicação na ortodontia
Other Titles: Study of mechanical proprieties and functional groups of a new nanocomposite for orthodontic application
Authors: Martins, Claudio Pinto
metadata.dc.contributor.advisor: Gouvêa, Cresus Vinicius Depes de
metadata.dc.contributor.advisorco: Almeida, Cristina Costa
Issue Date: 2018
Abstract: Objetivo do desta pesquisa foi avaliar a resistência a flexão de pontos entre resinas acrílicas comerciais e uma resina acrílica experimental à base de PMMA e Nanotubos de carbono. Foram confeccionados 10 corpos de prova de cada tipo de resina avaliada e conduzidos os ensaios. Foram realizados ensaios de flexão de 3 pontos para avaliação da resistência flexural e analise por FTIR, para verificação dos grupos funcionais. Foram encontradas diferenças significativas entres os grupos, o grupo experimental obteve bom resultado, superior à resina acrílica comercial. Foram encontradas diferenças estatisticamente significantes entre os grupos analisados no ensaio de resistência à flexão, nomeadamente, entre G1 e G2 e G1 e G3, o que sugere que as amostras contendo nanocarga podem ter seu uso clinico melhorado. Além dos resultados do FTIR, que comprovam que ambas as amostras, comerciais e experimentais se tratam de PMMA.
metadata.dc.description.abstractother: The aim of this study was to evaluate the flexural strength between commercial acrylic resins and an experimental acrylic resin based on PMMA and carbon nanotubes. Ten specimens of each type of resin evaluated were made and the tests conducted. Three-point flexural tests were performed to evaluate flexural strength and FTIR analysis to verify functional groups. Significant differences were found between the groups, the experimental group obtained a good result, superior to commercial acrylic resin. Statistically significant differences were found between the groups analyzed in the flexural strength test, namely between G1 and G2 and G1 and G3, which suggests that the nanotube containing samples may have improved clinical use. In addition to the results of the FTIR, which prove that both commercial and experimental samples are PMMA.
URI: https://app.uff.br/riuff/handle/1/10388
Appears in Collections:PPGO - Teses e Dissertações

Files in This Item:
File Description SizeFormat 
Dissertação Cláudio Pinto.pdf761.6 kBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons