Title: CARACTERIZAÇÃO QUÍMICA E CITOTOXICIDADE DE CIMENTOS ENDODÔNTICOS BIOCERÂMICOS
Authors: GUARNIER, ANA PAULA FERIANI
metadata.dc.contributor.advisor: Lins, Renata Ximenes
metadata.dc.contributor.advisorco: Andrade, Mônica Calixto de
metadata.dc.contributor.members: Lins, Renata Ximenes
Gomes, Cinthya Cristina
Laxe, Laísa Araujo Cortines
Issue Date: 2019
Abstract: Os cimentos endodônticos à base de silicato de cálcio foram recentemente introduzidos no mercado e por serem bioativos representam um novo conceito tanto para o preenchimento do canal radicular quanto para as aplicações que implicam interação com os tecidos periapicais. Neste estudo, objetivou-se analisar a composição química e avaliar o comportamento térmico e citotóxico de 3 novos cimentos endodônticos. Os cimentos biocerâmicos selecionados foram ProRooT ES (Dentsply); EndoSequence BC (Brasseler); NeoMTA (NuSmile); além do cimento de agregado trióxido mineral (do inglês Mineral Trioxide Agregate, MTA) MTA Branco (Angelus), escolhido como referência. Para avaliação da composição química, testes de análise de espectroscopia de infravermelho com transformada de Fourier (FTIR) e análise térmica foram empregados, enquanto a viabilidade celular foi avaliada pelo ensaio de metil-tiazol-difeniltetrazólio (MTT). Para os testes de citotoxicidade, células da linhagem 3T3 foram cultivadas em placas de 96 poços contendo meio Roswell Park Memorial Institute (RPMI-1640) e suplementado com 10 % de Soro Bovino Fetal durante 24 horas. Doze amostras de cada cimento foram confeccionadas em matrizes metálicas (3 mm de diâmetro x 2 mm de altura), e colocadas em contato com as células durante 24 h e 72 h em estufa de CO2 a 37 ºC. Como controle positivo foi empregado cimento de óxido de zinco e eugenol (OZE) e como controle negativo apenas meio de cultura. Com base nos resultados, não houve diferença estatisticamente significativa entre EndoSequence BC, Neo MTA e MTA Branco em todos os tempos testados (p < 0,05). ProRoot ES apresentou efeito citotóxico estatisticamente significante nos dois períodos testados (p < 0,05). A análise química dos cimentos mostrou similaridade entre NeoMTA e MTA Branco, o que está de acordo com as informações disponibilizadas pelo fabricante. Nossos resultados sugerem que o efeito citotóxico do cimento ProRoot ES pode estar relacionado a presença de maior teor de hidróxido de cálcio, que é calcinado na faixa de temperatura entre 400 e 500 ºC, com pico pronunciado da DTG em 420 ºC. Análises complementares são importantes, inclusive para identificar os compostos causadores de citotoxicidade e evitá-los em formulações futuras.
metadata.dc.description.abstractother: Calcium silicate-based endodontic substrates have been marketed and bioactives represent a new standard both for root canal filling and for applications involving interaction with periapical tissues. In this study, the objective was to investigate the chemical influence of cements and correlations to their biological behavior through the study of the cytotoxic effect. The bioceramic cements were created by ProRooT ES (Dentsply); EndoSequence BC (Brasseler); NeoMTA (NuSmile); In addition to aggregate mineral trioxide cement (White MTA, White MTA), choose as a reference. The analysis of Fourier Transform Infrared Spectroscopy (FTIR) and Thermal Analysis, Thermogravimetry or Thermogravimetric Analysis (TGA) and Differential Scanning Calorimetry (DSC), were performed, via cell viability were evaluated by assay of methyl-thiazole-diphenyltetrazolium (MTT). Cytotoxicity testis, 3T3 lineage cells were cultured in 96-well plates relative to the Roswell Park Memorial Institute (RPMI-1640) and supplemented with 10% Fetal Bovine Serum for 24 hours. Twelve samples of each cement were made in metal matrices (3 mm in diameter x 2 mm in height) and placed in contact with the cells for 24 h and 72 h in a CO2 oven at 37 ºC. As a positive control, zinc oxide and eugenol cement (OZE) were used and as a negative control only culture medium. Based on the results, there was no statistically significant difference between EndoSequence BC, Neo MTA and White MTA at all times tested (p <0.05). ProRoot ES presented statistically significant cytotoxic effect in the two periods tested (p <0.05). The chemical analysis of the cements showed similarity between NeoMTA and White MTA, which is in agreement with the information provided by the manufacturer; while EndoSequence BC and ProRoot ES presented some similarities, but also with peculiar and distinct characteristics. Our results suggest that the cytotoxic effect of ProRoot ES cement may be related to the presence of a higher content of calcium hydroxide, which is calcined in the temperature range between 400 and 500, with a pronounced DTG peak at 420 ºC. Further analyzes are important, including to identify cytotoxicity-causing compounds and to avoid them in future formulations.
URI: https://app.uff.br/riuff/handle/1/12685
Appears in Collections:PPGO - Dissertações - Nova Friburgo

Files in This Item:
File Description SizeFormat 
Dissertaçao - ANA PAULA FERIANI GUARNIER.pdfDissertaçao - CARACTERIZAÇÃO QUÍMICA E CITOTOXICIDADE DE CIMENTOS ENDODÔNTICOS BIOCERÂMICOS2.93 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.