Title: EFEITO DE UM DENTIFRÍCIO À BASE DE NANOHIDROXIAPATITA NA RUGOSIDADE DO ESMALTE BOVINO
Authors: REIS, PATRÍCIA QUEIROZ ROCHA DOS
metadata.dc.contributor.advisor: Barceleiro, Marcos de Oliveira
metadata.dc.contributor.advisorco: Calazans, Fernanda Signorelli
metadata.dc.contributor.members: Barceleiro, Marcos de Oliveira
Souza, Roberta Barcelos Pereira de
Miranda, Mauro Sayão de
Issue Date: 2016
Abstract: As nanopartículas de hidroxiapatita (nanoHAp) têm similaridade com os cristais de hidroxiapatita do esmalte dental e quando utilizadas para remineralizar e tratar a hipersensibilidade dentinária, associada ao flúor, parecem penetrar com maior facilidade no interior das microtrincas em esmalte, promovendo um selamento de qualidade e restaurando a microestrutura e a composição superficial dental. O objetivo deste trabalho foi avaliar in vitro o efeito de um dentifrício à base de nanoHAp na rugosidade superficial do esmalte bovino submetido a ciclagem de pH. Foram utilizados 12 discos de incisivos bovinos divididos em 2 grupos experimentais: Grupo 1 – dentifrício com flúor - Colgate Total 12 (Colgate-Palmolive Industrial LTDA) e Grupo 2 – dentifrício com nanoHAp - Megasonex (Grupo Goldspire LTDA). Os espécimes foram submetidos ao teste de escovação simulada em 30 ciclos, 2 vezes ao dia, e submetidos a um modelo de ciclagem de pH (desmineralização 6 h/ remineralização 18 h por dia) durante 14 dias. Todos os espécimes tiveram sua rugosidade superficial avaliada inicialmente e após o tratamento, utilizando um rugosímetro de bancada (Surftest SJ 201). Na análise estatística pela comparação múltipla entre pares, os testes de Bonferroni e Holm demonstraram que após 7 dias não houve diferença estatisticamente significativa no comportamento dos dentifrícios (p>0,05), porém após 14 dias, houve um aumento das médias de rugosidade no grupo 1 (dentifrício com flúor) estatisticamente significativo (p<0,05). Concluiu-se que o dentifrício com nanoHAp promoveu menor rugosidade superficial após 14 dias.
metadata.dc.description.abstractother: The hydroxyapatite nanoparticles (nanoHAp) have similarity with the hydroxyapatite crystals of the dental enamel and when used to remineralize and treat dental hypersensitivity, associated with fluoride, seems to easily penetrate inside the enamel micro cracks leading to a high quality sealing and restoring the microstructure and dental superficial composition. The aim of this research was to evaluate in vitro, the effects of dentifrices with nanoHAp on the roughness of the surface of bovine enamel submitted to a pH cycle. Twelve disks of bovine incisors were divided into 2 experimental groups: Group 1- dentifrice with fluoride - Colgate Total 12 (Colgate- Palmolive Industrial LTDA) and Group 2- dentifrice with nanoHAp – Megasonex (Goldspire Group LTDA). The specimens were submitted to 30 cycles of a simulated brushing test, twice a day, besides been submitted to pH cycle model (6 hours demineralization/18 hours remineralization a day) during 14 days. All specimens had their superficial roughness evaluated at baseline and after the treatment, using a bench rugosimeter (Surftest SJ 201). The statistical analyses by multiple comparison between pairs, Holm and Bonferroni test’s demonstrated that after 7 days there were no significant statistical difference in the behavior of the dentifrices (p>0,01), but after 14 days, there was an increase of medium roughness of group 1 (dentifrice with fluoride) statistically significant (p<0,05). It was concluded that the dentifrice with nanoHAp promoted less superficial roughness after 14 days.
URI: https://app.uff.br/riuff/handle/1/12688
Appears in Collections:PPGO - Dissertações - Nova Friburgo

Files in This Item:
File Description SizeFormat 
Dissertação Patrícia Queiroz.pdfDissertação - EFEITO DE UM DENTIFRÍCIO À BASE DE NANOHIDROXIAPATITA NA RUGOSIDADE DO ESMALTE BOVINO370.04 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.