Title: Síntese e caracterização de compósitos restauradores remineralizantes com partículas de nanohidroxiapatita
Other Titles: Synthesis and characterization of remineralizing restorative composites with nanohydroxyapatite particles
Authors: Reis, Renata Nunes Jardim
metadata.dc.contributor.advisor: Silva, Eduardo Moreira da
Issue Date: 2017
Abstract: Os objetivos deste trabalho foram avaliar o potencial remineralizante e caracterizar compósitos experimentais (CE) formulados com partículas (60 nm) de nanohidroxiapatita (n-HAp). Foram produzidos quatro CE a partir da mesma matriz polimérica (70% Bis-GMA e 30% TEGDMA), com substituição parcial das partículas de BaBSi (65% p/p) por n-HAp nas seguintes concentrações: 0 (E0, controle); 10 (E10); 20 (E20) e 30% (E30). O potencial remineralizante foi avaliado através da liberação de íons cálcio e fosfato, em soluções com diferentes pH (4; 5,5 e 7), utilizando espectroscopia de emissão atômica com plasma de nitrogênio induzido por micro-ondas e também através de micro-TC avaliando o conteúdo mineral de lesões. Foram caracterizadas as seguintes propriedades físico-químicas: grau de conversão (GC%), dureza Knoop (D), resistência à flexão (RF), módulo de elasticidade (ME) e padrão de translucidez (PT). Os dados foram submetidos à análise de variância e ao teste de Tukey (α=0,05). O pH influenciou a liberação de íons (7 < 5,5 < 4) (p < 0,05) e o aumento da concentração de n-HAp aumentou a liberação de íons (30% > 20% > 10%) (p < 0,05). Todos CE carregados com n-HAp foram capazes de remineralizar o esmalte adjacente às lesões quando comparados ao controle (p < 0,05). O ME não foi influenciado pela incorporação de n-HAp (p > 0,05). Em relação as demais propriedades os resultados foram significantes (p < 0,05): GC (E0 = E10 > E20 = E30), D e RF (E0 > E10 = E20 = E30) e PT (E0 = E10 > E20 > E30). Concluiu-se que a incorporação de n-HAp promoveu remineralização do esmalte, principalmente em pH cariogênico, sem prejudicar as propriedades físico-químicas do material.
metadata.dc.description.abstractother: The purposes of this study were to evaluate the remineralizing potential and characterize experimental composites (EC) formulated with nanohydroxyapatite (n-HAp) particles (60 nm). Four EC were produced from the same polymeric matrix (70% Bis-GMA and 30% TEGDMA), with partial replacement of BaBSi particles (65 wt.%) by n-HAp in the following concentrations: 0 (E0, control) ; 10 (E10); 20 (E20) and 30% (E30). The remineralizing potential was evaluated by calcium and phosphate ions release in solutions with different pH (4, 5.5 and 7), using an atomic emission spectroscopy instrument with microwave-induced nitrogen plasma and also through micro-CT evaluating lesions mineral content. The following properties were characterized: degree of conversion (DC%), microhardness (KHN), flexural strength (FS), elastic modulus (EM) and translucency (TP). Data were submitted to ANOVA and Tukey's test (α = 0.05). pH influenced the release of ions (7<5.5 <4) and the increase in n-HAp concentration increased the release of ions (30%> 20%>10%)(p <0.05). All EC loaded with n-HAp were able to remineralize the enamel adjacent to lesions when compared to control (p <0.05). EM was not influenced by the incorporation of n-HAp (p> 0.05). Regards other properties the results were significant (p <0.05): DC% (E0 = E10 > E20 = E30), KHN and FS (E0 > E10 = E20 = E30) and TP (E0 = E10 > E20 > E30). It was concluded that the incorporation of n-HAp promoted enamel remineralization, mainly at dangerously cariogenic pH, without jeopardizing physicochemical properties of the material.
URI: https://app.uff.br/riuff/handle/1/14750
Appears in Collections:PPGO - Teses - Niterói

Files in This Item:
File Description SizeFormat 
Tese Renata Jardim Reis.docx1.19 MBMicrosoft Word XMLView/Open


This item is licensed under a Creative Commons License Creative Commons