Title: Durabilidade da adesão à dentina de sistemas adesivos de condicionamento ácido total, contendo o inibidor de MMPS GM1489 em diferentes concentrações
Other Titles: Resin-dentin bonding stability of etch-and-rinse adhesive systems with different concentrations of MMPs inhibitor GM1489
Authors: Miranda, Maria Elisa da Silva Nunes Gomes
metadata.dc.contributor.advisor: Amaral, Cristiane Mariote
Issue Date: 2016
Abstract: O objetivo deste estudo foi avaliar o grau de conversão (GC%), a resistência de união (µTBS) à dentina (imediata e após 12 meses de estocagem) e a nanoinfiltração de um sistema adesivo experimental (EXP) e um comercial (SB), contendo diferentes concentrações do inibidor de MMPs GM1489:0, 1µM, 5µM e 10µM. O GC% dos sistemas adesivos foi medido por espectroscopia de FT-IR e calculado pela relação entre a área do sinal a 1639cm-1 e 1609cm-1 de filmes polimerizados e não polimerizados. Para avaliar µTBS à dentina, foram utilizados 48 molares humanos, que foram lixados até que a dentina oclusal fosse exposta. O esmalte periférico foi removido usando uma ponta diamantada, os sistemas adesivos foram aplicados e um bloco de resina composta foi construído em incrementos. Após 24h, os dentes foram cortados para obtenção de palitos com uma área de secção transversal de 1mm2. Metade dos palitos foi submetida ao ensaio de µTBS após 24h e a outra metade após 12 meses de estocagem. Foram separados 2 palitos de cada dente/tempo de estocagem para análise da nanoinfiltração. Os dados foram submetidos a Análise de Variância (2 fatores para GC% e 3 fatores para µTBS e nanoinfiltração) e Tukey HSD para contraste entre as médias (α=0,05). A incorporação do inibidor não afetou o GC% dos grupos EXP, mas SB5 e SB10 apresentaram maior GC% que SB0 e SB1. Todos os sistemas adesivos mantiveram a µTBS após 12 meses de estocagem, mas os grupos com as concentrações mais elevadas do inibidor (5µM e 10µM) apresentaram maior µTBS. A nanoinfiltração foi maior em SB0 do que em EXP10 nos tempos imediato e após 12 meses. Concluiu-se que as maiores concentrações de GM1489 (5µM e 10µM) podem aumentar o GC do SB e proporcionar maior µTBS após 12 meses de estocagem, independente do sistema adesivo testado, enquanto a concentração de inibidores não afetou a nanoinfiltração de cada sistema adesivo.
metadata.dc.description.abstractother: The aim of this study was to evaluate the degree of conversion (DC%), the dentin bond strength (µTBS) (immediate and after 12 months in water storage), and the nanoleakage of an experimental (EXP) and a commercial (SB) adhesive systems, containing different concentrations of the inhibitor of MMPs GM1489: 0, 1µM, 5µM and 10µM. The DC% was evaluated by FT-IR spectroscopy and the relation between sign area in 1639 cm-1 and 1609 cm-1 was calculated from polymerized and unpolymerized films. To evaluate dentin µTBS, 48 human molars were used, which were sand until exposition of occlusal dentin. The peripheral enamel was removed using a diamond bur, the adhesive systems were applied and a composite buildup was incrementally constructed. After 24h, the teeth were cut to obtain beams with a cross-sectional area of 1mm2. Half of the beans obtained were submitted to the µTBStest after 24h and the other half after 12 months of storage. From each tooth/time of storage were reserved 2 beans to nanoleakage test. The data were analyzed using ANOVA (2 factors for DC% and 3 factors for µTBS and nanoleakage) and Tukey’s HSD to compare means (α=0.05). The incorporation of the inhibitor not affected the DC% of the EXP groups, but the SB5 and SB10 groups showed higher µTBS values than SB0 and SB1. All adhesive systems maintained the µTBS after 12 months of storage, but the groups with higher concentrations of the inhibitor (5µM and 10µM) showed highest µTBS. The nanoleakage was higher in SB0 than in EXP10 in periods immediate and after 12 months. It was concluded that the highest concentrations of GM1489 (5µM and 10µM) may increase the DC% of SB andprovided greater μTBS after 12 months of storage regardless of the adhesive system tested, while the concentration of inhibitors did not affect nanoleakage of adhesive systems.
URI: https://app.uff.br/riuff/handle/1/16074
Appears in Collections:PPGO - Teses - Niterói

Files in This Item:
File Description SizeFormat 
Tese Maria Elisa Miranda.docx877.56 kBMicrosoft Word XMLView/Open


This item is licensed under a Creative Commons License Creative Commons