Title: Filmes de poli(álcool vinílico) e carboximetilcelulose para aplicação como curativos
Authors: Bosch, Hingred
metadata.dc.contributor.advisor: Futuro, Débora Omena
metadata.dc.contributor.advisorco: Costa, Valéria Gonçalves
metadata.dc.contributor.members: Leite, Márcia Christina Amorim Moreira
Ricci Jr, Eduardo
Issue Date: 16-Jan-2018
Abstract: Este trabalho teve como objetivo estudar a produção e as características de filmes poliméricos constituídos por poli(álcool vinílico) (PVA) e carboximetilcelulose (CMC) a serem utilizados posteriormente na produção de curativos primários para tratamento de feridas. Os polímeros escolhidos apresentam grau farmacêutico e suas misturas foram preparadas na proporção de PVA/CMC 9:1. Os polímeros inicialmente foram misturados em câmara fechada de mistura Haake Rheomix na intenção de promover misturas físicas. Nesta etapa foram estabelecidas 6 condições de mistura variando-se a temperatura da câmara e a velocidade de mistura. Esperava-se que ocorresse a fusão dos componentes durante o processo, o que não ocorreu. Para a formação dos filmes poliméricos foi testado o processo de prensagem em prensa hidráulica a quente e o processo de vazamento de soluções poliméricas em placas de vidro com posterior secagem. Não foram obtidos filmes adequados aos ensaios com a técnica de prensagem a quente, porém com técnica de vazamento se conseguiu a formação de bons filmes; com isso os filmes obtidos por esta técnica foram caracterizados quanto a propriedades físico-químicas, térmicas e mecânicas. Pode-se concluir que os filmes de PVA/CMC, obtidos pela técnica de vazamento, apresentaram características físicas, como a alta capacidade de inchamento em água e PBS, e mecânicas, como a resistência a ruptura e ao rasgamento, adequadas à utilização destes filmes como curativos para feridas
metadata.dc.description.abstractother: This work aimed to study the production and characteristics of poly(vinyl alcohol) (PVA) and carboxymethylcellulose (CMC) polymer films to be used later in the production of primary dressings for wound treatment. The polymers chosen were pharmaceutical grade and mixtures thereof were prepared in the ratio of 9:1 PVA / CMC. The polymers were initially mixed in a closed Haake Rheomix blend chamber in order to promote physical blends. In this step, 6 mixing conditions were established by varying the chamber temperature and the mixing speed. The melting of the components was expected to occur during the process, which did not occur. For the formation of the polymer films the pressing process was tested in a hot hydraulic press and the process of casting polymer solutions into glass plates with subsequent drying. It was not obtained films suitable for the tests with the technique of hot pressing, but with casting technique the formation of good films was achieved; and the films obtained by this technique are characterized by physical, chemical, thermal and mechanical properties. It can be concluded that the PVA/CMC films, obtained by the casting technique, presented physical characteristics, such as high swelling capacity in water and PBS, and mechanical, such as tear strength and tear resistance, suitable for the use of these films as wound dressings
URI: https://app.uff.br/riuff/handle/1/5515
Appears in Collections:PPG-CAPS - Teses e Dissertações

Files in This Item:
File Description SizeFormat 
HINGRED BOSCH.pdf2.95 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.