Title: Desenvolvimento e caracterização de pinos endodônticos biológicos obtidos a partir de dentina bovina
Other Titles: Development and characterization of biological bovine dentin posts
Authors: Penelas, Alice Gonçalves
metadata.dc.contributor.advisor: Guimarães, José Guilherme Antunes
Issue Date: 2016
Citation: PENELAS, Alice Gonçalves. Desenvolvimento e caracterização de pinos endodônticos biológicos obtidos a partir de dentina bovina. 2016. 52 f. Tese (Doutorado) - Curso de Odontologia, Universidade Federal Fluminense, Niterói, 2016.
Abstract: Este estudo objetivou desenvolver e caracterizar pinos endodônticos de dentina bovina (PD) e comparar seu desempenho ao de um pino de fibra de vidro (PFV / WhitePost DC 3) através das seguintes análises: módulo de elasticidade (E) e resistência à flexão (σ); resistência à fratura (RF) por ensaio de compressão a 135°; transmissão e espalhamento de luz (TL/EL) e sua influência na dureza Knoop (KHN) do cimento resinoso; e resistência de união (RU). Os PD foram confeccionados a partir da fresagem de blocos de dentina bovina. Para os testes, as coroas dos dentes bovinos foram removidas e o comprimento das raízes foi padronizado em 14mm. Os condutos radiculares foram preparados até 12mm e irrigados com NaOCl 2,5%. Para RF e KHN, após embutimento da raiz, o conduto radicular e a superfície dos PDs foram hibridizados (adesivo quimicamente ativável) e a superfície dos PFVs condicionada com H2O2 24%/1min e silanizada. Os pinos foram, então, fixados ao conduto com cimento resinoso dual. Para o teste de RU, os pinos foram cimentados utilizando-se o protocolo convencional e o autoadesivo. Os testes mecânicos de E, σ, RF e RU foram realizados em máquina de ensaios universal (EMIC DL2000; 1mm/min). Para as análises de TL e EL, os pinos foram transfixados por discos opacos de polietileno, deixando os 10mm apicais livres para a realização das medições. A extremidade cervical dos pinos foi irradiada (800mW/cm2) e TL e EL foram mensurados através de um espectrômetro, registrando o número de fótons, no intervalo entre 450-490nm do espectro eletromagnético. A KHN do cimento resinoso foi mensurada ao longo da extensão da linha de cimento e em sua extremidade mais apical. Os dados foram submetidos à análise de variância (5%) e ao teste de Scheffe (5%) para contraste. Os resultados foram: E: PD>PFV; σ: PD<PFV; RF: PD<PFV. A TL e o ES não foram observados nos PDs. Nos PFVs, o decaimento exponencial do EL foi observado nas regiões cervical (C), médio (M) e apical (A) e a TL na ponta apical (PA), de modo que PA>C>M>A. A KHN ao longo da linha de cimento foi estatisticamente semelhante em todas as regiões avaliadas independentemente do pino utilizado. RU: PD=PFV independentemente do protocolo de cimentação utilizado. Tendo em vista o desempenho observado, concluiu-se que PD podem ser uma alternativa promissora para a reabilitação de dentes tratados endodonticamente
metadata.dc.description.abstractother: This study aimed at evaluating the use of biological dentin (BD) posts, achieved by the milling of bovine roots, through the analyses of mechanical and optical properties. BD post performance were compared to those of fiber reinforced composite (FRC) posts in the following tests (n=10): a) elastic modulus (E) and flexural strength (σ) by three point bending test; b) fracture resistance (FR) by compressive load at 45º and failure pattern; c) light transmitting (LT) and light scattering (LS) ability and the influence in the Knoop Hardness (KHN) of the resin cement; d) bond strength (BS) by push-out test and failure pattern. Bovine teeth were decoronated and root length were standardized at 14mm. The canals were prepared and irrigated with 2.5% NaOCl. For FR and KHN, after root embedment, the root canal walls and BD surface were hybridized (self-cured adhesive) and FRC post surface were conditioned by 1min immersion in 24% H2O2 solution before silanization. Then, posts were fixed into the root canals using dual resin cement. For BS test, posts were luted using the conventional and self-adhesive protocol. A universal testing machine (EMIC DL2000; 1mm/min) was employed for the mechanical tests (E, σ, FR and BS). For the LT and LS analyses, opaque polyethylene discs transfixed the posts, leaving 10mm of the apical section for measurements. Posts cervical portion was irradiated (800mW/cm2) and a spectrometer recorded the number of photons transmitted or scattered for the range between 450-490ηm of the electromagnetic spectrum. Resin cement KHN was evaluated in several sites of the cement film. After normal distribution were checked (Shapiro-Wilk test), data were submitted to ANOVA (5%) and Scheffe post hoc test (5%). Results showed that: a) E: PD>PFV; b) σ: PD<PFV; c) RF: PD<PFV. LT and LS could not be observed for BD. For FRC posts, an exponential decay was observed for LS through the regions (cervical - C, middle - M and apical - A) and LT was observed at the apical tip (AT), leading to AT>C>M>A. Cement film KHN was statistically similar at all points of measurements independently of the type of the post employed. For BS, PD=PFV regardless the luting protocol used. It was concluded that teeth restored with BD posts exhibited lower fracture resistance than those restored with FRC post, KHN of resin cement was not influenced by the light transmitting ability of the post, and that the retention provided by the BD post is similar to the one provided by FRC post, independently of the luting protocol
URI: https://app.uff.br/riuff/handle/1/6537
Appears in Collections:PPGO - Teses e Dissertações

Files in This Item:
File Description SizeFormat 
Tese ALICE GONÇALVES PENELAS.pdf1.69 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons