Title: Avaliação in vitro do potencial elétrico superficial (molhabilidade) de amostras de titânio
Other Titles: In vitro evaluation of the potential electric superficial (wettability) of titanium samples
Authors: Ferreira, Neli Cunha
metadata.dc.contributor.advisor: Gouvêa, Cresus Vinicius Depes
metadata.dc.contributor.advisorco: Motta, Sergio H. G.
Issue Date: 2012
Abstract: O presente trabalho tem como objetivo determinar o ângulo de contato superficial de discos de titânio, da empresa SIN, com superfícies tratadas por subtração ácida e não tratadas, em contato com água destilada e cloreto de sódio (NaCl), bem como avaliar a influência do tratamento superficial na molhabilidade. As amostras de implantes foram representadas por unidades experimentais em forma de discos com 12mm de diâmetro por, no mínimo, 3mm de espessura, com tratamento de superfície específico por subtração ácida e tecnologia de descontaminação e armazenamento próprios da empresa SIN. Um grupo controle de titânio polido foi também preparado, semelhante ao implante de titânio puro comercialmente vendido, somente com descontaminação da superfície e limpeza. As superfícies das amostras foram comparadas em microscópio eletrônico de varredura (MEV), com objetivo de certificar a semelhança das mesmas. Logo após, as amostras foram analisadas em um goniômetro, no qual o ângulo de contato da água destilada e do NaCl formado na superfície do implante foram aferidos. Posteriormente, a rugosidade foi caracterizada por rugosímetro a laser. Devido à variabilidade encontrada nos dados, optou-se pela análise estratificada de cada fator pelo teste t de Student, no qual se observou que a superfície tratada por subtração ácida submetida ao contato com água destilada mostrou os melhores resultados (menor ângulo de contato – melhor molhabilidade)
metadata.dc.description.abstractother: The main purpose of this work was to determine the angle of two superficials contacts of the titanium disks from the SIN Company :one treated by acid subtraction and other non treated.Both surfaces were placed in contact with destiled water and NaCl in order to assess the influence of the superficial water treatment having as parameter the wetta shaped wetability level. Samples of implants represented by experimental units disk shaped 12mm of diameter.and a minimum 3mm of thickness which have been treated by specific surface treatement by acid subtratction and by the application of a decontamination technology and own storage by SIN company. It has also been prepared a control group of a titanium polished similar to the pure titanium commercial just with decontamination and cleaning processes. The surfaces were compared by eletronicmicrocospe of sweep, with the purpose to certificate if there are similarities among trhesamples.Then, after, the samples were analyzed in a goniometer, in order to assess the contact angle of the distilled water water and the NaCl shaped by the impant surface. Afterwards, the roughness was measured by a rugosimeter. In order to the variance founded on the static data, we adopted the stratified analysis of each factor by the t of student test where it has been observed that the surface treated by acid submitted to the contact with distilled water has shown the best results.(lower angle of caontact-better wettability)
URI: https://app.uff.br/riuff/handle/1/9969
Appears in Collections:PPGO - Teses e Dissertações

Files in This Item:
File Description SizeFormat 
Dissertação Neli Ferreira.pdf11.5 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons